Hydrogen embrittlement is a common, dangerous, and poorly understood cause of failure in many metal alloys. This article presents a model based on the correlation of mechanical properties to scanning electron microscopy fractography analysis of fracture surfaces in the presence of simultaneously active hydrogen embrittlement micro-mechanisms.